Influence of preoxidation on the corrosion of steels in liquid lead-bismuth eutectic

Citation data:

Corrosion, ISSN: 0010-9312, Vol: 60, Issue: 11, Page: 1031-1044

Publication Year:
2004
Usage 5
Abstract Views 5
Captures 8
Readers 7
Exports-Saves 1
Citations 10
Citation Indexes 10
Repository URL:
http://ideaexchange.uakron.edu/chemengin_ideas/447
DOI:
10.5006/1.3299217
Author(s):
R. S. Lillard; M. A. Hill; P. D. Dickerson; R. J. Hanrahan; C. Valot
Publisher(s):
NACE International
Tags:
Chemistry; Chemical Engineering; Materials Science; Biochemical and Biomolecular Engineering; Engineering
article description
Oxidation studies of martensitic/ferritic and austenitic steels have been conducted in static lead bismuth eutectic (LBE). Samples were preoxidized in an air/HO gas mixture prior to immersion in LBE. Preoxidation films grown on HT-9 at 800°C for 48 h had a bilayer structure, an outer Fe-rich layer, and an inner Cr-rich layer. Glancing angle x-ray diffraction data found that two distinct structures were present in this oxide: FeCrO spinel (cubic, face-centered cubic [fcc]) and (Cr,Fe)O (rhombohedral, corundum). Magnetite formation (Fe O) was ruled out. Immersion in LBE resulted in the growth of an Fe-rich film on top of the preoxidation layer. It was concluded that the growth mechanism was Fe interstitial transport from the metal/oxide interface. Preoxidized films grown on Type 316 (UNS S31600) stainless steel (SS) at 800°C for 64 h resulted in a Cr-rich inner layer and Fe-rich outer layer. X-ray diffraction found both FeCrO spinel (cubic) and (Cr,Fe)O, corundum (rhombohedral). In contrast to HT-9, angle-resolved x-ray diffraction found that the concentration of the FeCrO spinel decreased with distance from the metal oxide interface. Immersion of preoxidized Type 316 SS in LBE resulted in oxide growth; however, the new film formed in LBE was indistinguishable from the preoxidation layer. It was proposed that the enhanced oxidation of Type 316 SS as compared to HT-9 formed a FeCr O spinel layer near the oxide/metal interface results in a boundary-to-cation interstitial transport. © 2004, NACE International.