Fabrication and Mechanical Properties of an Optically Transparent Glass Fiber/Polymer Matrix Composite

Citation data:

Journal of Composite Materials, ISSN: 1530-793X, Vol: 26, Issue: 8, Page: 1181-1192

Publication Year:
1992
Captures 3
Readers 3
Citations 39
Citation Indexes 39
Repository URL:
http://scholarsmine.mst.edu/matsci_eng_facwork/875
DOI:
10.1177/002199839202600806
Author(s):
James R. Olson; Delbert E. Day; James O. Stoffer
Publisher(s):
SAGE Publications
Tags:
Materials Science; Engineering; Chemistry
article description
A composite with substantial optical transparency was produced by rein forcing poly(methyl methacrylate) (PMMA) with unidirectional borosilicate glass fibers. Optical transparency of the composite was achieved by matching the refractive index (n) of the glass fiber and polymer matrix to within ±0.002. The optical transmission of the composite decreased with increasing volume percentage of glass fibers. Composites con taining 30 volume percent of unidirectional 12 μm diameter fibers had a transmission at 589.3 nm of 20 percent measured through a 10 mm thickness. Composites containing 30 volume percent of 56 μm diameter fibers had an optical transmission of 45 percent. Type written text could be clearly read through the composite when it was laid directly on a printed page. Composites with 40 volume percent fiber had a flexural strength of 600 MPa which is six times greater than that of pure PMMA. The flexural modulus for the same composite was 18 MPa which is nine times greater than the 2 MPa measured for pure PMMA. The work of fracture was 110 kJ/mor more than double the 45 kJ/mfor pure PMMA. Suggestions are made for further improvements in the optical properties. © 1992, Sage Publications. All rights reserved.