Folding Graphene Film Yields High Areal Energy Storage in Lithium-Ion Batteries.

Citation data:

ACS nano, ISSN: 1936-086X, Vol: 12, Issue: 2, Page: 1739-1746

Publication Year:
2018
Captures 26
Readers 26
Social Media 7
Tweets 7
Citations 10
Citation Indexes 10
Repository URL:
http://scholarworks.unist.ac.kr/handle/201301/23906
PMID:
29350526
DOI:
10.1021/acsnano.7b08489
Author(s):
Wang, Bin; Ryu, Jaegeon; Choi, Sungho; Song, Gyujin; Hong, Dongki; Hwang, Chihyun; Chen, Xiong; Wang, Bo; Li, Wei; Song, Hyun-Kon; Park, Soojin; Ruoff, Rodney S. Show More Hide
Publisher(s):
American Chemical Society (ACS); AMER CHEMICAL SOC
Tags:
Materials Science; Engineering; Physics and Astronomy; folding; graphene composite films; high areal capacity; high mass loading; lithium-ion batteries
Most Recent Tweet View All Tweets
article description
We show that a high energy density can be achieved in a practical manner with freestanding electrodes without using conductive carbon, binders, and current collectors. We made and used a folded graphene composite electrode designed for a high areal capacity anode. The traditional thick graphene composite electrode, such as made by filtering graphene oxide to create a thin film and reducing it such as through chemical or thermal methods, has sluggish reaction kinetics. Instead, we have made and tested a thin composite film electrode that was folded several times using a water-assisted method; it provides a continuous electron transport path in the fold regions and introduces more channels between the folded layers, which significantly enhances the electron/ion transport kinetics. A fold electrode consisting of SnO/graphene with high areal loading of 5 mg cm has a high areal capacity of 4.15 mAh cm, well above commercial graphite anodes (2.50-3.50 mAh cm), while the thickness is maintained as low as ∼20 μm. The fold electrode shows stable cycling over 500 cycles at 1.70 mA cm and improved rate capability compared to thick electrodes with the same mass loading but without folds. A full cell of fold electrode coupled with LiCoO cathode was assembled and delivered an areal capacity of 2.84 mAh cm after 300 cycles. This folding strategy can be extended to other electrode materials and rechargeable batteries.