Effect of VOpromoter on characteristics and performance of NiO/CeOcatalyst in methane bi-reforming

In this work, a series of 10 wt% NiO/CeO2 catalysts (Ni/Ce) promoted by V2O5 with content varying in the range of 0-0.5 wt% was prepared by the co-impregnation method. The characteristics of the catalysts were investigated by several techniques including N2 physisorption (BET), X-ray diffraction (XRD), Raman spectroscopy, transmission electron microscopy (TEM), EDS mapping, carbon dioxide temperature-programmed desorption (CO2-TPD), and hydrogen temperature-programmed reduction (H2-TPR). The activity of the catalyst was studied in the micro-flow system in a temperature range of 550 C-800 C, the feedstock composition CH4/CO2/H2O of 3.0/1.2/2.4 and the weight hourly space velocity (WHSV) of 30,000 ml.h-1.g-1. Adding V2O5 additive, on the one hand increases the reducibility and basicity of Ni/Ce catalyst, on the other hand reduces oxygen vacancies and increases the crystal size of CeO2, leading to various effects on catalyst activity depending on its content. Ni/Ce catalyst promoted with 0.3 wt% of V2O5 was the best among tested ones, on which at reaction temperature of 700 C, the conversion of CH4 and CO2 reached 97% and 77% respectively, and the molar ratio of H2/CO was 2.1. Meanwhile, on non-promoted Ni/Ce catalyst, the corresponding quantities were 83%, 62% and 1.9, respectively. It is important to note that performance of both was stable for more than 30 h thanks to the better resistance to coke deposition and structural stability.